Type:MF1P-C□□□,
MF1G-C□□□
Color:Colored Series
●Characteristic and Application
The product is based on melamine modified urea formaldehyde
resin, to which cellulose as main filler, other additives such
as lubricant, curing agent are added. It is mainly used to make
insulation parts for low voltage electrical appliance or instrument,
household articles and mechanical parts. The product is suitable
for compression molding. MF1P-C□□□ appears in fine powder, MF1G-C□□□
appears in granular.
●Technical Properties
No.
|
Item
|
Test
standard
|
Unit
|
Value
|
1
|
Flexural strength
|
ISO178
|
MPa
|
≥80
|
2
|
Notched
impact strength
|
ISO179
|
KJ/m2
|
≥1.8
|
3
|
HDT
|
ISO75
|
℃
|
≥130
|
4
|
Water absorption
|
ISO62
|
mg
|
≤100
|
5
|
Molding shrinkage
|
ISO2577
|
%
|
0.5-0.9
|
6
|
Insulation
resistance
|
IEC60167
|
Ω
|
≥1010
|
7
|
Dielectric
strength
|
IEC60243-1
|
MV/m
|
≥3.5
|
8
|
CTI
|
IEC60112
|
V
|
600
|
9
|
Incandescence
resistance
|
ISO181
|
class
|
I
|
10
|
Arc
resistance
|
ASTM
D495
|
s
|
180
|
●Molding condition
|
|
|
|
|
Mold
temperature ℃
|
Molding
pressure MPa
|
Curing
time (s/mm)
|
140--150
|
80-160
|
60
|
|
|
●Package
and storage
Packed in kraft paper with plastic inner of 25kg net for dampproof.
The types, batch number, weight of the product are marked on the bags.
Material should be stored in a well-ventilated cool and dry place.
The storage temperature can not exceed 30℃. The storage time is half
a year since the material was produced. If the material is stored
longer than a.m. storage time, it should be checked again, the qualified
product could still be used. |
|
|